Flexible hydrocarbon rubber substrate finished with a thermosetting acrylic enamel

ABSTRACT

The flexible hydrocarbon rubber substrate finished with a thermosetting acrylic enamel is useful for automobile and truck bumpers, flexible filler panels located between the bumper and the chassis, flexible fender extensions, flexible exterior trim parts and other impact and energy absorbing parts and has the following structure: (1) A FINISH OF A CROSS-LINKED THERMOSETTING ACRYLIC ENAMEL OF (A) an acrylic polymer of an alkyl methacrylate having one-four carbon atoms in the alkyl group or styrene or mixtures thereof, an alkyl methacrylate having 2-12 carbon atoms in the alkyl group or an alkyl acrylate having 1-12 carbon atoms in the alkyl group, a hydroxy alkyl acrylate or methacrylate or a mixture thereof; and an Alpha , Beta -ethylenically unsaturated dicarboxylic acid; and (B) a heat reactive condensate such as an alkylated melamine formaldehyde resin or a polyisocyanate; firmly adhered to (2) A SURFACE ACTIVATED SATURATED OR UNSATURATED HYDROCARBON RUBBER SUCH AS ETHYLENE-PROPYLENE COPOLYMER RUBBER WHICH MAY INCLUDE A COPOLYMERIZED DIENE MONOMER, STYRENE-BUTADIENE COPOLYMER RUBBER, POLYBUTADIENE RUBBER, POLYISOPRENE RUBBER OR BUTYL RUBBER.

United States Patent 11 1 Hick [ 1 Oct. 15, 1974 FLEXIBLE HYDROCARBON RUBBER SUBSTRATE FINISHED WITH A THERMOSETTING ACRYLIC ENAMEL [75] Inventor: Robert M. Hick, Springfield, Pa.

[73] Assignee: E. I. du Pont de Nemours and Company, Wilmington, Del.

[22] Filed: Dec. 29, 1972 [21] Appl. No.: 319,897

[52] US. Cl 117/72, 117/77, 117/146, 260 /29.6 NR, 260/29.6 T [51] Int. Cl. B4lm 1/18, 1344c 3/02, 844d l/02 Primary Examiner-Ronald H. Smith Assistant Examiner-John L. Goodrow [57] ABSTRACT The flexible hydrocarbon rubber substrate finished with a thermosetting acrylic enamel is useful for automobile and truck bumpers, flexible filler panels located between the bumper and the chassis, flexible fender extensions, flexible exterior trim parts and other impact and energy absorbing parts and has the following structure:

(1) a finish of a cross-linked thermosetting acrylic enamel of (A) an acrylic polymer of an alkyl methacrylate having one-four carbon atoms in the alkyl group or styrene or mixtures thereof, an alkyl methacrylate having 2-12 carbon atoms in the alkyl group or an alkyl acrylate having 1-12 carbon atoms in the alkyl group, a hydroxy alkyl acrylate or methacrylate or a mixture thereof; and an a, B-ethylenically unsaturated dicarboxylic acid; and (B) a heat reactive condensate such as an alkylated melamine formaldehyde resin or a polyisocyanate; firmly adhered to (2) a surface activated saturated or unsaturated hydrocarbon rubber such as ethylene-propylene copolymer rubber which may include a copolymerized diene monomer, styrene-butadiene copolymer rubber, polybutadiene rubber,

polyisoprene rubber or butyl rubber.

16 Claims, 1 Drawing Figure FLEXIBLE HYDROCARBON RUBBER SUBSTRATE FINISHED WITH A THERMOSETTING ACRYLIC ENAMEL BACKGROUND OF THE INVENTION This invention is related to finished substrates and in particular to a flexible hydrocarbon rubber substrate finished with a thermosetting acrylic enamel.

The automobile and truck manufacturing industry'is currently utilizing bumpers of a flexible material, filler panels located between the bumper and the chassis, fender extensions, flexible exterior trim parts and other energy and impact absorbing parts to reduce damage in the event of a minor impact or a collision.

To provide the automobile or truck with a pleasing aesthetic appearance, a finish is applied to these parts. The parts are required to have a finish that has excellent adherence to the substrate, and is durable, flexible and weatherable. However, conventional hydrocarbon rubber substrates coated with enamels have been found unacceptable after short periods of use because of failure of the finish.

The novel coated substrate of this invention has excellent properties and utilizes a hydrocarbon rubber which has been surface activated and has a finish of a particular high quality thermosetting acrylic enamel.

SUMMARY OF THE INVENTION A flexible hydrocarbon rubber substrate finished with a 0.1 to mil thick finish of a cross-linked thermosetting acrylic enamel; wherein the enamel comprises (A) 70-95 percent by weight of anacrylic polymer consisting essentially of (1) 19-44 percent by weight, based on the weight of the acrylic polymer, of styrene or an alkyl methacrylate having one to four carbon atoms in the alkyl group;

(2) 50-75 percent by weight, based on the weight of the acrylic polymer, of an alkyl methacrylate having 6-12 carbon atoms in the alkyl group, or an alkyl acrylate having 2-12 carbon atoms in the alkyl group or a mixture of these constituents;

(3) 5 to percent by weight, based on the weight of the acrylic polymer, of a hydroxy alkyl acrylate or methacrylate having two to four carbon atoms in the alkyl group; and

(4) l to 20 percent by weight, based on the weight of the acrylic polymer, of an a,B-ethylenically unsaturated carboxylic acid;

(B) 5-30 percent by weight, based on the weight of the film-forming constituents, of a compatible cross-linking agent which is either an alkylated melamine formaldehyde resin having one to eight carbon atoms in the alkyl group or a polyisocyanate, and wherein the flexible hydrocarbon rubber substrate comprises surface activated saturated or unsaturated hydrocarbon rubber such as ethylenepropylene copolymer rubber which may include a copolymerized diene monomer, styrene-butadiene copolymer rubber, polybutadiene rubber, polyisoprene rubber or butyl rubber.

DESCRIPTION OF THE INVENTION This novel finished flexible substrate of this invention preferably has an enamel finish about 1.5 to 2.0 mils thick, optionally a primer layer 0.5 to 1.0 mils thick firmly adhered to a flexible hydrocarbon rubber substrate. Typically, the novel product of this invention is used as a bumper for automobiles and trucks and the substrate is firmly adhered to a steel member.

The drawing illustrates the invention Thethermosetting acrylic enamel finish 1 is firmly adhered to a primer 2 which is in adherence with the flexible hydrocarbon rubber substrate 3.

The coating composition used in this invention has a solids content of film-forming constituents of about 5-50 percent preferably, about 20-40 percent by weight. The novel composition can be clear or pigmented and if pigmented contains about 0.1-30 percent by weight pigment. Preferably, the pigmented compositions have a pigment to binder ratio of 5/100 to 40/ 100.

The film-forming constituents used in the coating composition comprise -95 percent by weight of an acrylic polymer, and correspondingly, 30-5 percent by weight of a compatible cross-linking agent, and preferably, about 85-90 percent by weight of the acrylic polymer and 10-15 percent by weight of the crosslinking agent. One preferred composition contains 87% by weight of the acrylic polymer and 13 percent by weight of an alkylated melamine formaldehyde resin. 7 The acrylic polymers utilized in the coating composition are prepared by conventional polymerization techniques in which the monomers are blended with solvents and polymerization catalysts and heated to about l 50C. for about 2-6 hours to form a polymer that has a relative viscosity of about 1.05-1.30, and preferably, about 1.06-1.20.

The relative viscosity is the value obtained by dividing the efflux time of the solution of the polymer by the efflux time of the solvent used to form the above polymer solution. The efflux times are measured according to the procedure of ASTM-D-445-46-T, Method B, using as the polymer solution 0.5 gram of the polymer dissolved in methlethyl keton to give 50 cubic centimeters of solution. The efflux is measured at a time temperatureof 30C. in a standard apparatus sold under the designation of modified Ostwald viscometer.

Typical solvents which are used to prepare the acrylic polymer and also used as diluent in the coating composition used in this invention are toluene, xylene, butyl acetate, ethyl acetate, acetone, methlethyl ketone, methyl-isobutyl ketone, ethyl alcohol, butyl alcohol and other aromatic hydrocarbons, cycloaliphatic hydrocarbons, esters ethers, ketones and alcohols, such as are conventionally used.

About 0.1-4 percent by weight, based on the weight of the monomers used to prepare the acrylic polymer, of a polymerization catalyst, is used. Typical catalysts are azo-bis-isobutyronitrile, azo-bis-( a-gammadimethyl-valeronitrile), benzoyl peroxide, t-butyl peroxy pivalate, di-tertbutyl peroxide and the like. Up to 5 percent by weight of a chain transfer agent can be used to control molecular weight such as dodecyl mercaptan or benzene thiol.

The acrylic polymer of the coating composition used in this invention contains 19-44 percent by weight, based on the acrylic polymer, of an alkyl methacrylate that has one to four carbons in the alkyl group or styrene or a mixture of the alkyl methacrylate and styrene. Typical alkyl methacrylates which can be used are 3 methyl methacrylate, ethyl methacrylate, propyl methacrylate, isopropyl methacrylate, butyl methacrylate, isobutyl methacrylate and the like. Preferably, the acrylic polymer contains 20 to 32 percent by weight of methyl methacrylate.

The acrylic polymer also contains 50-75 percent by weight, based on the weight of the acrylic polymer, of an alkyl methacrylate that has 6-12 carbon atoms in the alkyl group, or an alkyl acrylate that has 2-12 carbon atoms in the alkyl group or a mixture of the alkyl methacrylate and the alkyl acrylate. Typical alkyl methacrylates that can be used are hexyl methacrylate, 2-ethylhexyl methacrylate, octyl methacrylate, nonyl methacrylate, decyl methacrylate, and lauryl methacrylate. Typical alkyl acrylates that can be used are ethyl acrylate, propyl acrylate, butyl acrylate, isobutyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, octyl acrylate, nonyl acrylate, decyl acrylate, lauryl acrylate and the like. Preferably, the acrylic polymer contains 55 to 65 percent by weight of an alkyl acrylate having two to eight carbon atoms in the alkyl group, preferably butyl acrylate.

The acrylic polymer contains -20 percent by weight, preferably 8-12 percent by weight of a hydroxy alkyl acrylate or a hydroxy alkyl methacrylate or a mixture thereof that has two to four carbon atoms in the alkyl groups. Typical compounds of this type are hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxybutyl acrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, hydroxybutyl methacrylate and the like. Hydroxyethyl acrylate is preferred.

The acrylic polymer contains l-20 percent by weight of an mB-ethylenically unsaturated carboxylic acid, and preferably 1-5 percent by weight of the acid. Typical acids are acrylic acid, methacrylic acid, itaconic acid, crotonic acid, ethacrylic acid, propyl acrylic acid, and the like. Preferred are methacrylic acid and acrylic acid.

The following is one preferred acrylic polymer:

20 to 32 percent by weight of methyl methacrylate,

55 to 65 percent by weight of butyl acrylate, 8 to 12 percent by weight of hydroxyethyl acrylate,

l to 5 percent by weight of acrylic acid or methacrylic acid.

One particularly preferred polymer that gives a high quality finish is 61 percent butyl acrylate, 26 percent methyl methacrylate, percent 2-hydroxyethyl acrylate and 3 percent acrylic acid.

A blend of hard and soft acrylic polymers can be used in the acrylic enamel.

The cross-linking agent of the coating composition used in this invention is compatible with the acrylic polymer and can either be an alkylated melamine formaldehyde resin or a polyisocyanate. Typical alkylated melamine formaldehyde resins have one to eight carbon atoms in the alkyl group and are resins that are well known in the art. These resins are prepared by conventional techniques in which a lower alkyl alcohol such as methanol, ethanol, butanol, isobutanol, propanol, isopropanol, hexanol, 2-ethyl hexanol and the like is reacted with a melamine formaldehyde to provide pendent alkoxy groups.

Preferred melamine resins that are used are butylated melamine formaldehyde resins, methylated/butylated melamine formaldehyde resins and hexa( methoxymethyl) melamine.

An acid catalyst can be used in the coatingcomposition such as para-toluene sulfonic acid or butyl acid phosphate; An acid catalyst is needed if there is an absence of acid groups in the acrylic polymer or if a low temperature cure is required, or if a highly etherified melamine resin is used such as hexa(methoxymethyl)- melamine. v

A variety of organic polyisocyanates can be used in the coating composition and include aliphatic, cycloaliphatic, heterocyclic polyisocyanates. Typical polyisocyanates are, for example, methylene-bis-(4- cyclohexylisocyanate), tetramethylene diisocyanate, hexamethylene diisocyanate, ethylene diisocyanate, cyclohexylene-l,2-diisocyanate, and the like.

Polyisocyanates of a biuret, for example, the biuret of hexarnethylene diisocyanate made according to Mayer et al. US. Pat. No. 3,245,941, issued Apr. 12, 1966, can also be used.

Organic plasticizers can also be used in the thermosetting acrylic coating composition used in this invention in amounts up to l-lO percent by weight based on the weight of film-forming constituents. Monomeric and polymeric plasticizers can be used such as phthalate ester plasticizers, and in particular, alkyl and cycloalkyl ester phthalates in which the alkyl groups have 2-10 carbon atoms such as dioctyl phthalate, didecyl phthalate, butyl benzylphthalate, dicyclohexyl phthalate and mixtures thereof. Epoxidized soya bean oil, oil free and oil modified alkyds can also be used as plasticizers. Polyester resins such as alkylene glycol esters of adipic and benzoic acid, for example, ethylene glycol adipate benzoate, neopentyl glycol adipate benzoate, ethylene glycol adipate benzoate phthalate, can also be used in the coating composition of this invention.

The coating composition used in this invention can be pigmented. Typical pigments which can be used are metallic oxides, preferably titanium dioxide, zinc oxide, iron oxide, and the like, metallic flakes, such as aluminum flake, metallic powders, metallic hydroxides, Afflair pigments, i.e., mica coated with titanium dioxide, sulfates, carbonates, carbon blacks, silica, talc, china clay and other pigments, organic dyes and lakes.

Other compatible resins can be incorporated into the coating composition used in this invention such as vinyl chloride copolymers, polyurethanes, cellulose acetate butyrate, and silicone resins. Also, ultraviolet light stabilizers can be incorporated into the coating composition.

The thermosetting acrylic coating composition can be formed into a water based finish by neutralizing the polymer with ammonia or an amine such as diethylethanol amine and then adding water to form the composition. Any of the aforementioned additives, resins, plasticizers and pigments can be incorporated into the aqueous composition by using conventional techniques.

The resulting cross-linked acrylic finish must be flexible and durable. The finish should have a tensile strength of LOGO-2,000 pounds per square inch and an elongation at break of about -1 10%. This is an contrast to a conventional cross-linked acrylic finish which has an elongation at break of 4-8%.

A primer composition can be used in the flexible hydrocarbon rubber substrate of this invention to improve adhesion of the thermosetting acrylic enamel to the substrate. Typical primers that can be used are of a hydroxyl terminated polyalkylene ether glycol crosslinked with an aromatic diisocyanate and a polyester chain-extended with an organic diisocyanate and crosslinked with an alkylated melamine formaldehyde resin.

Preferred primers of the above types are as follows: a hydroxyl terminated polypropylene ether glycol cross-linked with toluene diisocyanate and an isophthalate polyester chain-extended with methylenebis-(cycloxyl isocyanate) and cross-linked with alkylated melamine formaldehyde resin.

Any of the aforementioned pigments and other additives can be added to the primers. Preferably, carbon black and extender pigments are used in the primer.

The flexible hydrocarbon rubber substrate may be any one of the well-known saturated or unsaturated hydrocarbon elastomers, i.e., those containing only carbon and hydrogen. It is preferred to use one of the ethylene-propylenc copolymer elastomers, particularly one that is made sulfur curable by the inclusion of 1-10 percent by weight non-conjugated diene, because of their better resistance to oxidative and thermal aging; how ever, butyl rubber, styrene-butadiene rubber, polybutadiene rubber or polyisoprene rubber (either natural or synthetic) may also be used. Particularly preferred among the ethylene-propylene rubbers are those copolymers containing 50-75 weight percent ethylene, 25-45 weight per cent propylene, and 2-8 weight percent non-conjugated diene such as 1,4-hexadiene, 5-ethylidene-2-norbornene or dicyclopentadiene.

These hydrocarbon rubbers must be surface activated by one of the chemical, electrical or flame treatments which are known to activate hydrocarbon surfaces so that they are wet more easily by and adhere more tenaciously to the coatings applied thereon. Such treatments include surface oxidation by exposure of surface to oxidizing chemicals such as chromates, permanganates or ozone; etching by strong acid; exposure of the surface to electrical discharge or ionizing or nonionizing radiation of various kinds of treatment with flame. A particularly preferred method of activation is the exposure of the surface to ultraviolet lightin the presence of a photo-activator such as benzophenone.

Surface activation treatments of this type for the hydrocarbon rubber substrate may include the provision of thin layers of activating or coupling chemicals or resins. Photo-activators with ultraviolet light treatment as mentioned above can be used. Other activating or coupling chemicals that can be used include polymerizable ethylenically unsaturated monomers, polyisocyanates or isocyanate terminated polymers, epoxides or epoxide resins and polyethers.

One preferred process to provide an activated surface on ethylene-propylene-diene rubbers comprises:

(1) cleaning the rubber surface with a solvent;

(2) drying the surface;

(3) applying a 5-10 percent benzophenone solution so that 1.0-2.0 milligrams of benzophenone per square inch will be deposited and then drying the surface;

(4) exposing the surface to ultraviolet light, preferably a wave length band of 365 t 5 nm and then applying a primer or the acrylic enamel topcoat.

To prepare the novel coated article of this invention,

the primer if used is applied to conventional techniques to the hydrocarbon rubber substrate by the usual application methods such as spraying, electrostatic spraying, dipping, brushing, flow-coating and the like. The primer is then baked at 95 to 145C. for 5 to minutes. The thermosetting acrylic enamel is then applied by one of the aforementioned application methods and baked at 95 to 130C. for 15 to 60 minutes.

The following Examples illustrate the invention. All quantities are on a weight basis unless otherwise indicated.

Portion l is charged into a reaction vessel equipped with a stirrer, a reflux condenser, a thermometer and a heating mantle and heated to its reflux temperature of about C. Portion 2 is premixed and added over a -minute period while maintaining the reaction mixture at its reflux temperature (80C.). Portion 3 is then added and the reaction mixture is held at its reflux temperature for an additional two hours and then cooled to room temperature.

The resulting polymer solution has a polymer solids content of about 49 percent. The polymer is of methyl methacrylate/butylacrylate/2-hydroxyethyl acrylate/acrylic acid in a weight ratio of 26/61/ 10/3 and has a relative viscosity measured at 0.5 percent solids in methylethyl ketone at 25C. of about 1.135 and an acid number of about 28-30.

A mill base is prepared as follows:

Parts By Weight Portion 1 Polymer solution (60% solids of a polymer of styrene/butyl acrylate/2- hydroxyethyl acrylate/acrylic acid weight ratio 50/38/8/4 in a blend of hydrocarbon solvents and xylene having 21 Gardner Holdt viscosity of X-Z measured at 25C.) 9.00 Toluene 4.50 Anhydrous lsopropanol 3.60 V.M. & P. naphtha 3.90 Portion 2 Titanium dioxide pigment 63.00 Portion 3 Polymer solution (described above) 16.00 Total 100.00

A coating composition is prepared by blending together the following ingredients:

The resulting coating composition has 37 second viscosity measured in a No. Zahn Cup at 25C.

The physical properties of the above coating composition are tested using a standard sample and are as follows:

Tensile Strength 1620 pounds per square inch 60% Elongation at break The coating composition is reduced with a mixture of ethyl acetate and ethylene glycol monobutyl ether to a spray viscosity of seconds measured with a No. 2 Zahn Cup. The composition is then sprayed onto a inch thick Nordel rubber substrate which is a rubber of an ethylene-propylene diene polymer and baked for minutes at 120C. to give a finish about 1.8 mils in thickness.

Before the rubber is coated with the composition, it is surface treated using the following procedure:

( l The rubber substrate is immersed in a 1.5 percent solution of Ridoline 72 manufactured by Amchem Products, Incorporated, Ambler, Pa;

(2) The substrate is rinsed as follows: Three 15 second rinses with the last rinse being with deionized water;

(3) The substrate is drained and dried;

(4) The dried substrate is sprayed with a 10 percent solution of benzophenone dissolved in xylene to deposit about 1.0-2.0 milligrams of dry benzophenone per square inch of surface of the substrate;

(5) The benzophenone coated surface is exposed to a quartz-jacketed mercury vapor containing 0.050.4 joules/square centimeter of radiation in the wave length band of 365i Snm and allowed to cool to about 50C.

The rubber substrate with the activated surface then is sprayed with the above composition and baked as indicated above. The resulting finish onthe flexible rubber substrate has good gloss and an excellent appearance, and has excellent resistance to cracking and chipping of the finish from the substrate and also has excellent weatherability and can withstand outdoor exposure to Florida sunlight for extended periods of time.

A second set of surface treated Nordel rubber substrates are sprayed with a polyurethane primer having a 21 percent solids content and a pigment to binder ratio of 80/100 in which the binder is a hydroxyl terminated polypropylene ether glycol and a cross-linking agent of toluene diisocyanate and the pigment is a blend of carbon black and extender pigment. The primed substrates are baked for 30 minutes at 93C. The above prepared coating composition is reduced to a spray viscosity as above and is sprayed onto the primed substrate and baked for 30 minutes at 120C. The resulting finish has good gloss and an excellent appearance and the finish has excellent resistance to cracking and chipping from the substrate even when the substrate is flexed and the finish has excellent weatherability and can withstand outdoor exposure to Florida sunlight for extended periods of time.

A third set of surface treated Nordel rubber sub strates are sprayed with a polyurethane primer in which the primer has a solids content of 25-40 percent and a pigment to binder ratio of 30/ in which the binder is an isophthalate polyester chain extended with methylene bis(cyclohexylisocyanate) and uses an alkylated melamine formaldehyde as a cross-linking agent. The primed substrates are baked for 30 minutes at C. The above prepared coating composition is reduced to a spray viscosity as above and is sprayed onto the primed substrate and baked for 30 minutes at 120C. The resulting finish has good gloss and an excellent appearance and the finish has excellent resistance to cracking and chipping from the substrate even when the substrate is flexed. The finish has excellent weatherability and can withstand outdoor exposure to Florida sunlight for extended periods of time.

EXAMPLE 2 Parts By Weight Pigmented coating composition 250 (prepared in Example 1 Diethylethanol amine 5 Deionized water 250 Total 505 The pigmented coating composition is charged into a mixing vessel and then the diethylethanol amine is added with mixing and mixing is continued for 5 minutes. Then the deionized water is slowly added over a 3 minute period with mixing to cause inversion and subsequent reduction to spray viscosity. The resulting aqueous coating composition is sprayed onto a Nordel rubber substrate that is surface treated as in Example 1 and dried under the following conditions:

air dried for 5 minutes and then baked at 88C. for 30 minutes and then baked at C. for 30 minutes.

The resulting finish has an excellent appearance and a 60 gloss of 74. The finish has excellent resistance to cracking and chipping from the substrate when flexed and the finish has excellent weatherability.

EXAMPLE 3 The coating composition is prepared by blending together the following ingredients:

The resulting coating composition has a solids content of 51 percent and a pigment to binder ratio of 4/100. The composition is reduced to a spray viscosity with a conventional reducing thinner and sprayed onto a Nordcl rubber substrate that is surface treated as in Example 1 and primed with a pigmented polyurethane primer of the ether glycol cross linked with toluene diisocyanate described in Example 1. The coating substrate is baked for 30 minutes at 120C. The resulting finish has a good appearance and excellent adhesion to the flexible substrate and does not chip or crack when the substrate is flexed and has excellent outdoor durability.

EXAMPLE 4 A high quality finish can be prepared by blending the polymer solution prepared in Example 1 with a polyisocyanate cross-linking agent for example the biuret of hexamethylene diisocyanate. The constituents are blended together so that the ratio of isocyanate groups to hydroxy groups of the polymer is in the range of 0.521 to l.l:l. The resulting finish can be pigmented with the same mill base as described in Example 1. The resulting composition is reduced to a spray viscosity and applied to a Nordel rubber substrate which is surface treated as in Example 1 and then baked using the same baking conditions as in Example 1. The Nordel rubber substrate can be primed with either of the primers described in Example 1 and then coated as above. In any case, the resulting finish will have properties similar to the finish of Example 1, i.e., good gloss, excellent appearance, good adhesion, excellent resistance to flexing, cracking and chipping and good weatherability.

The invention claimed is:

l. A flexible hydrocarbon rubber substrate finished with 0.1- mil thick finish of a cross-linked thermosetting acrylic enamel; wherein the film-forming constituents of the enamel comprise:

A. 70-95 percent by weight, based on the weight of the film-forming constituents, of an acrylic polymer consisting essentially of 1. 19-44 percent by weight, based on the weight of the acrylic polymer, of an alkyl methacrylate having one to four carbon atoms in the alkyl group or styrene, or a mixture thereof:

2. 50-75 percent by weight, based on the weight of the acrylic polymer, of an alkyl methacrylate having 6-12 carbon atoms in the alkyl group or an alkyl acrylate having 2-12 carbon atoms in the alkyl group or a mixture thereof;

3. 5-20 percent by weight, based on the weight of the acrylic polymer, of a hydroxy alkyl acrylate or a hydroxy alkyl methacrylate or a mixture thereof having two to four carbon atoms in the alkyl groups; and

4. l to 20 percent by weight, based on the weight of the acrylic polymer, of an a,B-ethylenically unsaturated carboxylic acid;

B. 5-30 percent by weight, based on the weight of the film-forming constituents, of a compatible alkyl- 'ated melamine formaldehyde having one to eight carbon atoms in the alkyl group or a polyisocyanate;

wherein the flexible hydrocarbon substrate comprises a surface activated saturated or unsaturated hydrocarbon rubber from the group of ethylene-propylene copolymer rubber, ethylene-propylene-diene copolymer rubber, styrene-butadiene copolymer rubber, polybutadiene rubber, polyisoprene rubber and butyl rubber.

2. The flexible rubber substrate of claim 1 in which a primer layer is between the rubber substrate and the finish of the acrylic enamel.

3. The flexible rubber substrate of claim 1 in which the thermosetting acrylic enamel finish comprises A. -90 percent by weight, based on the weight of the film-forming constituents, of an acrylic polymer consisting essentially of 1. 20-32 percent by weight, based on the weight of the acrylic polymer, of methyl methacrylate;

2. 55-65 percent by weight, based on the weight of the acrylic polymer, of butyl acrylate;

3. 8-12 percent by weight, based on the weight of the acrylic polymer, of hydroxy ethyl acrylate;

4. 1-5 percent by weight, based on the weight of the acrylic polymer of acrylic acid;

B. 10-15 percent by weight, based on the weight of the film-forming constituents, of a butylated melamine formaldehyde resin.

4. The flexible rubber substrate of claim 3 in which the substrate comprises a surface activated ethylenepropylenediene copolymer rubber.

5. The flexible rubber substrate of claim 3 in which the substrate comprises a styrene-butadiene copolymer rubber.

6. The flexible rubber substrate of claim 3 in which the substrate comprises a polybutadiene rubber.

7. The flexible rubber substrate of claim '3 in which the substrate comprises a polyisoprene rubber.

8. The flexible rubber substrate of claim 3 in which the substrate comprises a butyl rubber.

9. The flexible substrate of claim 3 in which a primer layer is between the rubber substrate and the finish of the acrylic enamel and comprises a polyurethane of a hydroxy terminated polyalkylene ether glycol and an aromatic diisocyanate.

10. The flexible substrate of claim 9 in which the primer layer consists essentially of a hydroxy terminated polypropylene ether glycol and toluene diisocyanate.

11. The flexible substrate of claim 3 in which a primer layer is between the rubber substrate and the finish of the acrylic enamel and comprises a polyurethane of a polyester chain extended with an organic diisocyanate and cross-linked with an alkylated melamine formaldehyde resin.

12. The flexible rubber substrate of claim 3 in which the substrate comprises a surface activated ethylenepropylene-diene polymer rubber which consists essentially of 50-75 percent by weight ethylene, 25-45 percent byweight propylene and 2-8 percent by weight of a non-conjugated diene selected from the group consisting essentially of 1,4-hexandiene, 5-ethylidene-2- norbornene and dicyclopentadiene.

13. The flexible rubber substrate of claim 12 in which the substrate of the surface activated ethylenepropylene-diene copolymer has deposited on its surface benzophenone and the surface has been exposed to ultraviolet light to form a surface activated substrate.

percent by weight pigment and the film-forming constituents of the enamel consist essentially of A. 85-90 percent by weight, based on the weight of the film-forming constituents, of an acrylic polymer consisting essentially of l. -32 percent by weight, based on the weight of the acrylic polymer, of methyl methacrylate; 2. 55-65 percent by weight, based on the weight of the acrylic polymer, of butyl acrylate; 3. 8-12 percent by weight, based on the weight of the acrylic polymer, of hydroxy ethyl acrylate; 4. 1-5 percent by weight, based on the weight of the acrylic polymer of acrylic acid; B. 10-15 percent by weight, based on the weight of the film-forming constituents, of a butylated melamine formaldehyde resin,

wherein the flexible hydrocarbon rubber substrate phatic diisocyanate gr a cy cloaliphatic diisocyanat e 16. The flexible rubber substrate of claim 15 in which the diisocyanate is the biuret of hexamethylene diisocyanate. 

1. A FLEXIBLE HYDROCARBON RUBBER SUBSTRATE FINISHED WITH 0.1-10 MIL THICK FINISH OF A CROSS-LINKED THERMOSETTING ACRYLIC ENAMEL; WHEREIN THE FILM-FORMING CONSTITUENTS OF THE ENAMEL COMPRISES: A. 70-95 PERCENT BY WEIGHT, BASED ON THE WEIGHT OF THE FILM-FORMING CONSTITUENTS, OF AN ACRYLIC POLYMER CONSISTING ESSENTIALLY OF
 1. 19-44 PERCENT BY WEIGHT BASED ON THE WEIGHT OF THE ACRYLIC POLYMER, OF AN ALKYL METHYACRYLATE HAVING ONE TO FOUR CARBON ATOMS IN THE ALKYL GROUP OR ALKYLENE, OR A MIXTURE THEREOF:
 2. 50-75 PERCENT BY WEIGHT, BASED ON THE WEIGHT OF THE ACRYLIC POLYMER, OF AN ALKYL METHARCYLATE HAVING 6-12 CARBON ATOMS IN THE ALKYL GROUP OR AN ALKYL ACRYLATE HAVING 2-12 CARBON ATOMS IN THE AKYL GROUP OR A MIXTURE THEREOF;
 3. 5-20 PERCENT BY WEIGHT, BASED ON THE WEIGHT OF THE ACRYLIC POLYMER, OF A HYDROXY ALKYL ACRYLATE OR A HYDROXY ALKYL METHACRYLATE OR A MIXTURE THEREOF HAVING TWO OR FOUR CARBON ATOMS IN THE ALKYL GROUPS; AND
 4. 1 TO 20 PERCENT BY WEIGHT BASED ON THE WEIGHT OF THE ACRYLIC POLYMER, OF AN A,B-ETHYLENICALLY UNSATURATED CARBOXYLIC ACID; B. 5-30 PERCENT BY WEIGHT, BASED ON THE WEIGHT OF THE FILM-FORMING CONSTITUENTS, OF A COMPATIBLE ALKYLATED MELAMINE FORMALDEHYDE HAVING ONE TO EIGHT CARBON ATOMS IN THE ALKYL GROUP OR A POLYISOCYANATE; WHEREIN THE FLEXIBLE HYDROCARBON SUBSTRATE COMPRISES A SURFACE ACTIVATED SATURATED OR UNSATURATED HYDROCARBONS RUBBER FROM THE GROUP OF ETHYLENE-PROPYLENE COPOLYMER RUBBER, ETHYLENE-PROPYLENE-DIENE COPOLYMER RUBBER, STYRENEBUTADIENE COPOLYMER RUBBER, POLYBUTADIENE RUBBER, POLYISOPRENE RUBBER AND BUTYL RUBBER.
 2. 50-75 percent by weight, based on the weight of the acrylic polymer, of an alkyl methacrylate having 6-12 carbon atoms in the alkyl group or an alkyl acrylate having 2-12 carbon atoms in the alkyl group or a mixture thereof;
 2. 55-65 percent by weight, based on the weight of the acrylic polymer, of bUtyl acrylate;
 2. The flexible rubber substrate of claim 1 in which a primer layer is between the rubber substrate and the finish of the acrylic enamel.
 2. 55-65 percent by weight, based on the weight of the acrylic polymer, of butyl acrylate;
 3. 8-12 percent by weight, based on the weight of the acrylic polymer, of hydroxy ethyl acrylate;
 3. The flexible rubber substrate of claim 1 in which the thermosetting acrylic enamel finish comprises A. 85-90 percent by weight, based on the weight of the film-forming constituents, of an acrylic polymer consisting essentially of
 3. 8-12 percent by weight, based on the weight of the acrylic polymer, of hydroxy ethyl acrylate;
 3. 5-20 percent by weight, based on the weight of the acrylic polymer, of a hydroxy alkyl acrylate or a hydroxy alkyl methacrylate or a mixture thereof having two to four carbon atoms in the alkyl groups; and
 4. 1 to 20 percent by weight, based on the weight of the acrylic polymer, of an Alpha , Beta -ethylenically unsaturated carboxylic acid; B. 5-30 percent by weight, based on the weight of the film-forming constituents, of a compatible alkylated melamine formaldehyde having one to eight carbon atoms in the alkyl group or a polyisocyanate; wherein the flexible hydrocarbon substrate comprises a surface activated saturated or unsaturated hydrocarbon rubber from the group of ethylene-propylene copolymer rubber, ethylene-propylene-diene copolymer rubber, styrene-butadiene copolymer rubber, polybutadiene rubber, polyisoprene rubber and butyl rubber.
 4. 1-5 percent by weight, based on the weight of the acrylic polymer of acrylic acid; B. 10-15 percent by weight, based on the weight of the film-forming constituents, of a butylated melamine formaldehyde resin, wherein the flexible hydrocarbon rubber substrate comprises a surface activated ethylene-propylene-diene polymer rubber which consists essentially of 50-75 percent by weight ethylene, 25-45 percent by weight propylene and 2-8 percent by weight of a non-conjugated diene selected from the group consisting essentially of 1,4-hexandiene, 5-ethylidene-2-norbornene and dicyclopentadiene, and wherein the flexible hydrocarbon rubber substrate is surface activated by having deposited thereon benzophenone and having the surface exposed to ultraviolet light.
 4. The flexible rubber substrate of claim 3 in which the substrate comprises a surface activated ethylene-propylenediene copolymer rubber.
 4. 1-5 percent by weight, based on the weight of the acrylic polymer of acrylic acid; B. 10-15 percent by weight, based on the weight of the film-forming constituents, of a butylated melamine formaldehyde resin.
 5. The flexible rubber substrate of claim 3 in which the substrate comprises a styrene-butadiene copolymer rubber.
 6. The flexible rubber substrate of claim 3 in which the substrate comprises a polybutadiene rubber.
 7. The flexible rubber substrate of claim 3 in which the substrate comprises a polyisoprene rubber.
 8. The flexible rubber substrate of claim 3 in which the substrate comprises a butyl rubber.
 9. The flexible substrate of claim 3 in which a primer layer is between the rubber substrate and the finish of the acrylic enamel and comprises a polyurethane of a hydroxy terminated polyalkylene ether glycol and an aromatic diisocyanate.
 10. The flexible substrate of claim 9 in which the primer layer consists essentially of a hydroxy terminated polypropylene ether glycol and toluene diisocyanate.
 11. The flexible substrate of claim 3 in which a primer layer is between the rubber substrate and the finish of the acrylic enamel and comprises a polyurethane of a polyester chain extended with an organic diisocyanate and cross-linked with an alkylated melamine formaldehyde resin.
 12. The flexible rubber substrate of claim 3 in which the substrate comprises a surface activated ethylene-propylene-diene polymer rubber which consists essentially of 50-75 percent by weight ethylene, 25-45 percent by weight propylene and 2-8 percent by weight of a non-conjugated diene selected from the group consisting essentially of 1,4-hexandiene, 5-ethylidene-2-norbornene and dicyclopentadiene.
 13. The flexible rubber substrate of claim 12 in which the substrate of the surface activated ethylene-propylene-diene copolymer has deposited on its surface benzophenone and the surface has been exposed to ultraviolet light to form a surface activated substrate.
 14. The flexible rubber substrate of claim 1 in which the thermosetting acrylic enamel finish contains 0.1-30 percent by weight pigment and the film-forming constituents of the enamel consist essentially of A. 85-90 percent by weight, based on the weight of the film-forming constituents, of an acrylic polymer consisting essentially of
 15. The flexible rubber substrate of claim 1 in which the cross-linking agent for the acrylic enamel is an aliphatic diisocyanate or a cycloaliphatic diisocyanate.
 16. The flexible rubber substrate of claim 16 in which the diisocyanate is the biuret of hexamethylene diisocyanate. 